Abstract
Plasma transferred arc technique was used for the surface modification of 14.5wt%-Cr cast iron. The objective of this work was to investigate the microstructural and hardness changes, caused by plasma surface melting and post heat treatment. The processing parameters were: arc current 250A, voltage 60V, working gas – argon, scanning speed: 0.25m/min which ensured the surface temperature about 1500°C. The study involved optical microscopy, SEM/EDS, XRD, Finite element modeling (FEM), Thermo-Calc calculations and microhardness measurements. A modified melted layer of about 230μm depth was obtained comprising 10-fold refined dendrites and eutectic carbides as compared with conventional casting. The as plasma treated layer contained supersaturated austenite and “fresh” eutectic “austenite+M7C3” crystallized after melting. The latter formed fine networks or “massive” areas comprising fine carbide plates and fibers. A shell/core structure in coarse dendrites was revealed with different contents of Cr and secondary carbides. Post-heat treatment (isothermal holding at 800°C for 2h followed by oil quenching) resulted in precipitation of nano-sized secondary carbides in austenite followed by martensite transformation, which significantly increased the microhardness of the melted layer. Phase transformation phenomena and sequences are discussed based on Finite Element/Thermo-Calc modeling, EDS-investigation and hardness profile results.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.