Abstract
The structure of 3 nm and 15 nm diamond-like carbon films, grown on Si(001) by filtered cathodic arc, was studied by angle-resolved X-ray photoelectron spectroscopy (ARXPS) and transmission electron microscopy (TEM). The ARXPS data was deconvolved by employing simultaneous-fitting, which allowed for a clear deconvolution of the Si 2p and C 1s spectra into their different chemical contributions. An analysis of the take-off angle dependence of the peak intensities allowed for an independent identification of the physical origin of the chemical species. It was shown that the C 1s peak at 283.3 eV and the Si 2p peak at 99.6 eV correspond to SiC, and that the C/Si interface of the 3 nm film consists of a stoichiometric approximately 1 nm SiC layer. To quantify the sp(3)-sp(2) ratio it was necessary to take into account not only their associated C 1s XPS-peak intensities, but also their take-off angle dependence. The thickness of the films obtained through ARXPS closely agrees with cross-sectional TEM images.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.