Abstract
The TaC, HfC, and Hf-Ta-C coatings are successfully prepared by non-reactively DC magnetron sputtering. The effects of working pressure and deposition temperature on the structure and mechanical properties of Ta-Hf-C coating are analyzed. The scratch performance of the Ta-Hf-C coating deposited on 304 stainless steel and tungsten substrates are investigated. Results show the hardness and elastic modulus of Ta-Hf-C solid solution coating both increase to 37.8 ± 1.1 GPa and 435.8 ± 13.8 GPa due to the solid solution strengthening effect. Plastic deformation resistance H3/E2 of Ta-Hf-C coating can reach 0.285, which is more than twice that of binary coating. Furthermore, the scratch performance and failure mechanism show that Ta-Hf-C coating has a weaker plastic deformation resistance on soft substrate and low friction characteristic (0.01) on hard substrate, which implies that Ta-Hf-C coating is a good protective coating that can be applied to cutting tools.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.