Abstract
TiN/TaN coatings, consisting of alternating nanoscaled TiN and TaN layers, were deposited using magnetron sputtering technology. The structure, hardness, tribological properties and wear mechanism were assessed using X-ray diffraction, microhardness, ball-on-disc testing and a 3-D surface profiler, respectively. The results showed that the TiN/TaN coatings exhibited a good modulation period and a sharp interface between TiN and TaN layers. In mutilayered TiN/TaN coatings, the TiN layers had a cubic structure, but a hexagonal structure emerged among the TaN layers besides the cubic structure as the modulation period went beyond 8.5 nm. The microhardness was affected by the modulation period and a maximum hardness value of 31.5 GPa appeared at a modulation period of 8.5 nm. The coefficient of friction was high and the wear resistance was improved for TiN/TaN coatings compared with a homogenous TiN coating, the wear mechanism exhibited predominantly ploughing, material transfer and local spallation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.