Ln0.6Sr0.4Co0.8Fe0.2O3 (Ln=La, Pr, Nd, Sm) perovskite-type complex oxides were synthesized using a glycine-nitrate process, and the structure, electrical conducting and thermal expansion properties of the resulting ceramics were examined with regard to the nature of the lanthanide cations. The results indicated that the La, Pr and Nd specimens had a rhombohedral symmetry, while an orthorhombic structure was determined for the Sm specimen. The pseudo-cubic lattice constant decreased with smaller lanthanide cations. It was found that the electrical conducting properties declined with decreasing lanthanide cation size. Fortunately, all the compositions remained rather high electrical conductivities exceeding 650 Ω−1·cm−1 in the intermediate temperature range (600–800 °C). An appreciable thermal expansion increase at high temperatures was detected for all the compositions. Decreasing the size of the lanthanide cations resulted in an increase of thermal expansion. With respect to the high electrical conductivities, the Ln0.6Sr0.4Co0.8Fe0.2O3 oxides are considered to be acceptable as mixed conducting component in composite cathode designs together with doped ceria electrolytes.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.