Abstract
Ba6FeNb9O30 ceramics were synthesized by a standard solid-state sintering process. X-ray powder diffraction (XRD) refinements were carried out to analyze the crystal structure, and the dielectric, ferroelectric and magnetic properties were investigated and discussed. The tetragonal tungsten bronze structure in space group P4bm was determined with the lattice parameters: a = 12.597(6) A, b = 12.597(6) A, c = 3.989(1) A. An extremely high dielectric constant was indicated at higher temperatures, and it dropped quickly when the sample was cooled down through a critical temperature, and this critical temperature showed strong frequency dependence. This dielectric relaxation was more obviously observed in the dielectric loss curve. The nonlinear magnetic hysteresis curve was observed in the present ceramics at 5 K, which was related to the magnetic ions (Fe3+) in tungsten bronze structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.