Abstract
(Ba 0.68− x Sr 0.308Bi 0.006Na 0.006Mg x )(Ti 0.99Sn 0.01)O 3 ceramics were synthesized by solid-state reaction process. The samples ( X ≤ 0.010) are a mixture of cubic (major) and rhombohedral (minor) phases. The rhombohedral phase causes a large dielectric loss in low temperature regions and plays an important role in diffuse phase transition of ceramics. While X > 0.010, the rhombohedral phase decreases and gradually disappears. The dielectric loss of ceramics in the low temperature regions decreases, and the samples change from the diffuse phase transition to the phase transition of second order, and then to of first order. In the temperature range of 270–370 °C, intrinsic conduction dominates conductivity of ceramics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.