Abstract
YbMn0.17Si1.88 was synthesized from the reaction of ytterbium, manganese, and silicon using indium as a flux. The average structure of YbMn0.17Si1.88 was refined in the monoclinic space group P21, with a = 4.0107(8) Å, b = 3.8380(8) Å, c = 14.458(3) Å, β = 97.97(3)°, R1/wR2 = 0.0296/0.0720. The structure can be described as the intergrowth of three AlB2-type layers and one BaAl4-type layer. Magnetic susceptibility measurements suggest that the ytterbium atoms in YbMnxSi2-x exist in a mixed valent or intermediate valent state. YbMn0.17Si1.88 shows weak antiferromagnetic ordering below ∼4.5 K. The magnetic interactions between the Mn and Yb atoms in YbMn0.17Si1.88 are evident from the magnetic susceptibility measurements performed at low field. A negative magnetization is observed on warming and a positive magnetization on cooling. The heat capacity data suggest moderate heavy fermion behavior.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.