Abstract
Abstract Positron annihilation spectroscopy was carried out on nanocrystalline silver. Both lifetime and Doppler broadening were measured. High-resolution electron microscopy observations were also performed. Diffuse vacancy clusters, the sizes of which correspond to two to four vacancies, and voids of 1–5 nm diameter, were found to reduce the average atomic density of the grain boundary. Some grains grew to a diameter larger than about 70 nm during annealing the specimen from 50 to 100°C. A large fraction of the diffuse vacancy clusters and voids in the boundaries remained after annealing at 400°C. They were stabilized during annealing probably by gaseous atoms.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.