Abstract
AbstractHydrogenolysis of n-butane and CO hydrogenation were used to charac-terize the behavior of TiO2supported Rh in the SMSI state. The Rh was supported on a model support consisting of nonporous spherical particles of TiO2. The simple geometry of the support permits the metal crystallites to be imaged ‘edge-on’ in a transmission electron microscope. This allows detailed examination of the metal surface and the metal-oxide interface as a function of pretreatment. After high temperature reduction in H2, there is no significant change in the morphology of the Rh crystallites. However, the presence of amorphous overlayers 0.2–0.4 nm thick is clearly evident on the Rh surface. These overlayers can only be partially removed after oxidation at 473 K. The presence of these overlayers is well correlated with the drop in hydrogen chemisorption and altered reactivity. While the butane hydrogenolysis activity of Rh is considerably suppressed in the SMSI state, the CO hydrogenation activity is increased by a factor of 3. The H2uptake and the butane hydrogenolysis activity can be only partially restored after oxidation at 473 K. Treatment at 773 K in oxygen is necessary for restoring the pre-SMSI behavior.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.