Abstract
Mullite has achieved outstanding importance as a material for both traditional and advanced ceramics because of its favourable thermal and mechanical properties. Mullite displays various Al to Si ratios referring to the solid solution Al 4+2 x Si 2−2 x O 10− x , with x ranging between about 0.2 and 0.9 (about 55 to 90 mol% Al 2O 3). Depending on the synthesis temperature and atmosphere mullite is able to incorporate a number of transition metal cations and other foreign atoms. The crystal structure of mullite is closely related to that of sillimanite, which is characterized by chains of edge-connected AlO 6 octahedra running parallel to the crystallographic c-axis. These very stiff chains are cross-linked by tetrahedral chains consisting of (Al,Si)O 4 tetrahedra. In more detail: Parallel to a the tetrahedra are linked to the relatively short more stiff Al–O(A, B) bonds, whereas parallel b they are linked parallel to the relatively long more compliant Al–O(D) bonds. In mullite some of the oxygen atoms bridging the tetrahedra are removed for charge compensation. This gives rise to the formation of oxygen vacancies and of T 3O groups (so-called tetrahedral triclusters). The anisotropy of the bonding system of mullite has a major influence on the anisotropy of its physical properties. For example: • the highest longitudinal elastic stiffness is observed parallel c, but lower ones parallel a and especially parallel b, • the maximum of the thermal conductivity occurs parallel c, but maller ones parallel a and especially parallel b, • large thermal expansion especially parallel b, • fastest crystal growth and highest corrosion parallel c. Heat capacity and thermal expansion measurements of mullite display reversible anomalies in the temperature range between about 1000 and 1200 °C. It is believed that tetrahedral cations, bridging O atoms, and O vacancies undergo dynamical site exchange processes at high temperatures. At lower temperatures the dynamic disorder may transform to a static one. Diffraction experiments revealed that also partially ordered states may exist.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.