Abstract
Structure and properties are studied for binary blends composed of poly(lactic acid) (PLA) and poly(butylene succinate) (PBS). The rheological measurements in the molten state reveal that the entanglement molecular weight of PLA is lower than that of PBS. Further, the interfacial tension of the immiscible blend system is evaluated employing a rheological emulsion model and found to be 3.5 [mN/m]. Moreover, thermal analysis directly detects that addition of PBS enhances the crystallization of PLA even though PBS is in a molten state. Further, the cold-crystallization for quenched blends occurs at lower temperature than that for a quenched PLA. This would be attributed to the nucleating ability of PBS, leading to generation of PLA crystallites during the quench operation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.