Abstract

Experimental studies including microhardness and electrical conductivity measurements, transmission electron microscopy (TEM) together with atom probe tomography (APT) have been carried out for exploring the influence of tin (Sn) trace addition on the structure and precipitation hardening response in Al-Cu based alloy after either casting or cold or hot rolling. It is shown that the Sn trace addition refines the Al2Cu phase in an as-cast Al3.5Cu0.1Sn (wt.%) alloy. The alloy showed an increase by about 20% the peak hardness (~120 HV) for both cast and wrought products as well as significant reduction in the aging time to peak hardness (from 12 h to 2 h at 175 °C). According to the TEM and APT, the increased hardness is due to the formation of much finer θ′-phase precipitates with high number density.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.