Abstract
The 0.9Pb(ZrxTi1−x)O3-0.07Pb(Mn1/3Nb2/3)O3-0.03Pb(Sb1/2Nb1/2)O3(PZT-PMnN-PSN) ceramics were prepared by columbite method. The phase structure of the ceramic samples was analyzed. Results show that the pure perovskite phase is in all ceramics specimens. The effect of the Zr/Ti ratio on the region of morphotropic phase boundary for PZT-PMnN-PSN ceramics was studied. Experimental results show that the phase structure of ceramics changes from tetragonal to rhombohedral with the increase of the content of Zr/Ti ratio in the system. The composition of PZT-PMnN-PSN ceramics near the morphotropic phase boundary obtained is the ratio of Zr/Ti: 49/51. At this ratio, the ceramic has the optimal electromechanical properties: thekp=0.61, theεmax=29520, thed31=-236 pC/N, theQm=2400, high remanent polarization (Pr=49.2 μC·cm−2), and low coercive fieldEc=10.28 kV·cm−1.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.