Abstract
The dual-phase membrane of La 0.15Sr 0.85Ga 0.3Fe 0.7O 3− δ –Ba 0.5Sr 0.5Fe 0.2Co 0.8O 3− δ (LSGF–BSCF) was prepared successfully. This membrane was characterized with X-ray diffraction (XRD), scanning electron microscopy (SEM) and electron probe micro-analyzer (EPMA). This membrane has a dense dual-phase structure: LSGF being the dense body of this membrane and BSCF as another phase running along the LSGF body. This structure is favorable for the oxygen permeation through the membrane. The oxygen permeation test shows that the oxygen permeation flux of LSGF–BSCF membrane ( J O 2 =0.45 ml/min cm 2, at 915 °C) is much higher than that of LSGF membrane ( J O 2 =0.05 ml/min cm 2). Thickness dependence of oxygen permeation indicates that the oxygen permeation is controlled by the bulk diffusion. Compared to pure BSCF, the dual-phase membrane of LSGF–BSCF is stable in reducing atmosphere.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.