Structure and oxidation state of hematite surfaces reacted with aqueous Fe(II) at acidic and neutral pH

Abstract

Structural changes and surface oxidation state were examined following the reaction of hematite (0 0 1), (0 1 2), and (1 1 0) with aqueous Fe(II). X-ray reflectivity measurements indicated that Fe(II) induces changes in the structure of all three surfaces under both acidic (pH 3) and neutral (pH 7) conditions. The structural changes were generally independent of pH although the extent of surface transformation varied slightly between acidic and neutral conditions; no systematic trends with pH were observed. Induced changes on the (1 1 0) and (0 1 2) surfaces include the addition or removal of partial surface layers consistent with either growth or dissolution. In contrast, a <1 nm thick, discontinuous film formed on the (0 0 1) surface that appears to be epitaxial yet is not a perfect extension of the underlying hematite lattice, being either structurally defective, compositionally distinct, or nanoscale in size and highly relaxed. Resonant anomalous X-ray reflectivity measurements determined that the surface concentration of Fe(II) present after reaction at pH 7 was below the detection limit of approximately 0.5–1 μmol/m 2 on all surfaces. These observations are consistent with Fe(II) oxidative adsorption, whereby adsorbed Fe(II) is oxidized by structural Fe(III) in the hematite lattice, with the extent of this reaction controlled by surface structure at the atomic scale. The observed surface transformations at pH 3 show that Fe(II) oxidatively adsorbs on hematite surfaces at pH values where little net adsorption occurs, based on historical macroscopic Fe(II) adsorption behavior on fine-grained hematite powders. This suggests that Fe(II) plays a catalytic role, in which an electron from an adsorbed Fe(II) migrates to and reduces a lattice Fe(III) cation elsewhere, which subsequently desorbs in a scenario with zero net reduction and zero net adsorption. Given the general pH-independence and substantial mass transfer involved, this electron and atom exchange process appears to be a significant subsystem within macroscopic pH-dependent Fe(II) adsorption.