Abstract
Zirconium nitride precipitates, ZrN, were produced by internally nitriding single crystals of niobium containing various (small) amounts of zirconium, at 1473 K in nitrogen gas at a partial pressure of about 5 x 10 -3 Pa. The structural changes that occurred during annealing treatments after nitridation were investigated using transmission electron microscopy. Electron diffraction patterns show that ZrN particles have the Bain type orientation relationship with the matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.