Structure and Optical Band-Gap Energies of Ba0.5Sr0.5TiO3 Thin Films Fabricated by RF Magnetron Plasma Sputtering

Abstract

The structure and optical band-gap energies of Ba0.5Sr0.5TiO3 (BST0.5) thin films prepared on SiO2/Si and fused quartz substrates by RF magnetron plasma sputtering were studied in terms of deposition temperature and film thickness. Highly (100)-oriented BST0.5 thin films were successfully sputtered on a Si substrate with an approximately 1.0-µm-thick SiO2 layer at a deposition temperature of above 450°C. The optical transmittance of BST0.5 thin films weakly depended on the magnitude of X-ray diffraction (XRD) peak intensity. This is very helpful for monolithic integration of BST0.5 films for electrooptical functions directly onto a SiO2/Si substrate. The band-gap energies showed a strong dependence on the deposition temperature and film thickness. It was mainly related to the quantum size effect and the influence of the crystallinity of thin films, such as grain boundaries, grain size, oriented growth, and the existence of an amorphous phase. The band-gap energy values, which were much larger than those of single crystals, decreased with the increase in the deposition temperature and the thickness of BST0.5 thin films. The band-gap energy of 311-nm-thick amorphous BST0.5 thin film was about 4.45 eV and that of (100)-oriented BST0.5 thin film with a thickness of 447 nm was about 3.89 eV. It is believed that the dependence of the band-gap energies of the thin films on the crystallinity for various values of deposition temperature and film thickness means that there could be applications in integrated optical devices.