Abstract
In this work four different microstructures were obtained by unidirectional solidification of Fe-Cr-C eutectic alloys. Conditions for zone coupled growth were determined in alloys containing approximately 30 wt pct chromium. Furthermore, mechanical testing indicated that the maximum strength was exhibited by Fe-30Cr-C alloys with cerium or titanium additions. These alloys had the largest volume fraction of eutectic fibers and their ultimate tensile strength was of the order of 3250 MPa. Correlations between the rate of crystal growth(u) and fiber spacing (λ) or tensile strength(Rm) were found and an expression of the typeRm = Aλ-b2 was obtained whereb 2 varied between 0.283 and 0.685. Finally, manganese or chromium (35 wt pct Cr) additions did not lead to appreciable improvements in composite strength for this alloy system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.