Abstract
The relationship between structure, electrical and magnetic properties of thin poly(p-xylylene) - nickel nanocomposite films with Ni concentrations from 5 to 30 vol% was studied. It was found that metal concentration strongly affects size and oxidation state of the nanoparticles and composites morphology. At nickel concentration below 5 vol% the nanoparticles are oxidized to NiO and homogeneously distributed within fine-grained polymer matrix. An increase of Ni concentration up to 10 vol% results in the development of coarse-grained morphology with preferable localization of the nanoparticles at the boundaries of polymeric grains. And finally, in the composite films with nickel concentration above 20 vol%, the fine-grained morphology is observed again, but the nanoparticles are mainly metallic. Effect of the filler content on electrical and magnetic properties of the nanocomposites was elucidated showing that they are determined by percolation phenomenon with the threshold value of about 10 vol%. The well-pronounced magnetic hysteresis as well as ferromagnetic ordering were observed at Ni content above the percolation threshold. The diagrams of magnetic properties of these composites as a function of composition and temperature were elaborated. It was demonstrated that film annealing can be used to control magnetic properties of the composites and strongly enhance magnetoresistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.