Abstract
The structure and magnetic properties of PrFe10Mo2Nx compounds prepared by melt spinning have been investigated. A single-phase structure of ThMn12-like has been obtained in ribbons quenched at velocities vs below 40 m/s. The desired ThMn12 structure is considerably more stable for Pr(Fe, Mo)12 compounds than for Nd(Fe, Mo)12 compounds. Only at higher speeds than 50 m/s the PrFe10Mo2 ribbons quench into TbCu7-like compound of which Curie temperature is about 580 K. Annealing temperatures in excess of 1023 K are required to form ThMn12 crystal structure for the ribbons melt spun at 50 m/s. Upon nitrogenation at 723 K, the Curie temperatures increase to 663 and 580 K for TbCu7- and ThMn12-like nitrides, respectively. A coercivity of 3.3 kOe with a magnetization up to 118 emu/g at a field of 20 kOe has been obtained in the present ribbons.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.