Abstract
Ti1-xFexO2 nanocrystals with x = 0.01, 0.02, 0.03 were prepared via a nonaqueous synthesis route. X-ray diffraction, transmission electron microscopy and high resolution transmission electron microscopy characterization confirmed the formation of anatase-phase nanocrystals with the average crystallite sizes of around 10 nm. The lattice constants alternate with the increase of the Fe content and no iron clusters were generated. X-ray photoelectron spectroscopy measurements showed that the substitutional Fe ions present mainly the valence of +3. The magnetic hysteresis loops measured at room temperature (RT) 300K showed that all the doped samples are atypically ferromagnetic, and the coercivity (Hc) of all the Fe-doping samples is around 0.1 T. An interpretation for the intrinsic RT ferromagnetism is put up based on the free carriers and defects induced interaction between Fe3+ ions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.