Abstract
Al-Ni-Co alloy has been widely applied in various industrial fields due to its excellent thermal and magnetic stability. In this paper, new Al-Ni-Co ribbons are prepared by simple processes combining melt-spinning with annealing, and their phase transition, microstructure and magnetic properties are studied. The results show that after as-spun ribbons are annealed, the grain size of ribbons increases from 1.1 ± 0.3 μm to 4.8 ± 0.8 μm, but still much smaller than that of the bulk Al-Ni-Co alloy manufactured by traditional technologies. In addition, some rod-like Al70Co20Ni10-type, Al9Co2-type and Fe2Nb-type phases are precipitated at grain boundaries; simultaneously, the distinct spinodal decomposition microstructure with periodic ingredient variation is thoroughly formed in all grains by the reaction of α → α1 + α2. Furthermore, the α1 and α2 distribute alternately like a maze, the Fe-Co-rich α1 phase holds 35.9–47.3 vol%, while the Al-Ni-rich α2 phase occupies the rest. Finally, the coercivity of annealed ribbons can reach to 485.3 ± 76.6 Oe. If the annealed ribbons are further aged at 560 °C, their Hc even increases to 738.1 ± 81.0 Oe. The coercivity mechanism is discussed by the combination of microstructure and domain structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.