Abstract
A novel BaLu2Al2Ga2SiO12:Ce3+ persistent phosphor was designed and synthesized through hetero-valence substituting Ba2+-Si4+ ion pair for Lu3+-Al3+ one in the Lu3Al3Ga2O12. XRD and Rietveld refinement results confirm the garnet typed crystal structure. SEM information shows that the constituent elements are uniformly distributed on the irregular particles. Under 360 or 430 nm excitation, the samples exhibit broad emission bands peaking at 510 nm. The luminescence intensity reaches to the maximum at 6 mol% Ce3+ doping content, and an internal quantum efficiency of 51.2% is achieved. The concentration quenching between Ce3+ ions is mainly originated from exchange interaction. Moreover, the phosphors exhibit bright cyan afterglow for minutes after removing the blue-light excitation source. The persistent luminescence decay process is studied by thermoluminescence spectra. The persistent luminescence mechanism and optical information writing and reading process are also discussed to explore the application in optical information storage.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call