Abstract
Ferroelectric ceramics, SrBi2Nb2O9 (SBN), Sr0.8Cu0.2Bi2Nb2O9 (SCBN) and Sr0.8K0.1Na0.1Bi2Nb2O9 (SKNBN) were prepared by a solid state reaction process. X-ray diffraction analysis shows that the alkali and Cu almost diffuse into the SBN lattice to form a solid solution during sintering and some slight secondary phases was detected. The effect of alkali and Cu on dielectric properties of the SBN ceramics was discussed. The dielectric loss factor of (K,Na) doped SBN ceramics degraded considerably to 0.01 and their frequency and temperature stabilities were enhanced. The dielectric constant was enhanced by approximately 60% and the Curie temperature (Tc) was also improved for Cu doped SrBi2Nb2O9 ceramics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.