Abstract
The coatings were prepared by the means of Pt and Pt/Pd galvanizing, followed by vapor phase aluminizing at 1050°C. Microstructural and phase analysis revealed that all the investigated coatings consisted mainly of β-NiAl phase, however the Pt-modified aluminide coating also contained PtAl2 phase and pure platinum precipitates. The cross-sectional microstructure of the coatings was zonal and composed of β-NiAl phase zone and the diffusion zone. The Pt modified aluminide coating's cross-section also incorporated an outermost zone consisting of β-NiAl and PtAl2 phases. The concentration profiles proved that both Pt and Pd contents decrease gradually inwards the modified coatings. Cyclic oxidation tests at 1100°C proved that Pt/Pd-modified aluminide coatings exhibit the best performance under cyclic conditions. The analysis of oxidation kinetics curves showed that the course of simple aluminide coating's oxidation is slightly different from that of Pt- and Pt/Pd-modified aluminide coatings.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.