Abstract
The structure and properties of vacuum-arc multi-period composite coatings of the MeN/Cu system (where Me is Cr, Zr, and Nb) are studied. It was found that at the smallest nanolayer thickness (about 8…10 nm) of composites in the layers of all systems, only a phase with an fcc lattice is formed, without a pronounced texture in the nitride layers. For ZrN and CrN, the phases with an fcc lattice are equilibrium, and for NbN, they are nonequilibrium. An increase in the thickness of nitride layers leads to the appearance of a texture in ZrN/Cu and CrN/Cu systems and the formation of an equilibrium ε-NbN phase in the layers of the NbN/Cu system. Tests for corrosion resistance in the environment of the formation of chloride ions showed that the coatings are anodic reaction. The best corrosion properties were obtained for coatings with the smallest layer thickness (about 8…10 nm).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.