Abstract
AbstractThe structure and compatibility of poly(vinyl alcohol)‐silk fibroin (PVA/SF) blend films were analyzed by differential scanning calorimetry (DSC), thermomechanical (TMA) and thermogravimetric (TGA) analysis, x‐ray diffractometry, and scanning (SEM) and transmission (TEM) electron microscopy. DSC curves of PVA/SF blend films showed a major endothermic peak at 220°C, along with a peak at 280°C. These endotherms were assigned to the thermal decomposition of the ordered PVA elements and to the thermal degradation of silk fibroin, respectively. The PVA/SF blends behaved in a manner intermediate to the pure components, as suggested by both contraction expansion and sample weight retention properties recorded by TMA and TGA measurements. The IR absorption spectra of the blends were identified as purely a composite of the absorption bands characteristic of both PVA and SF pure polymers. The X‐ray diffraction patterns of PVA/SF blends showed overlapping spacing due to PVA and SF. A dispersed phase formed by spherical particles of 3–7 μm diameter was observed by SEM and TEM. All these findings suggest that PVA and SF are incompatible. © 1994 John Wiley & Sons, Inc.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Polymer Science Part B: Polymer Physics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.