Abstract

Tin oxide films were deposited on amorphous SiO2/Si and Si (100) substrates by ion-assisted deposition (IAD) at various ion beam potentials (VI) at room temperature and a working pressure of 8 × 10−5 torr. The structural and chemical properties of the as-grown tin oxide films were investigated to determine the effects of the oxygen ion/atom arrival ratio (Ri). X-ray diffraction patterns indicated that the as-grown films with different average energy per atom (Eave) showed different growth directions. The as-grown films with oxygen/Sn ratio (NO/NSn) of 2.03 and 2.02 had preferred orientation of (101) and (002), respectively. In addition, the as-grown film with low Ri was amorphous. Comparison of the observed d spacings with those for standard SnO2 samples, indicated that the crystalline as-grown films had compressive and tensile stress depending on Eave. In transmission electron microscopy analysis, a buffer layer of amorphous tin oxide was observed at the interface between the substrate and the film, and the crystalline grains were grown on this buffer layer. The crystalline grains were arranged in large spherical clusters, and this shape directly affected surface roughness. Rutherford backscattering spectroscopy spectra showed that the tin oxide thin films were inhomogeneous. The density of films decreased and the porosity and oxygen trapped in the films increased with increasing Ri. The densest film had about 6% porosity.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.