Supramolecular ferroelectric cocrystal of phenazine (Phz) with chloranilic acid (H2ca), which exhibits three successive phase transitions, have been characterized by the interplay between their structural transformations and solid-state acid–base (proton transfer) reactions (Figure) [1]. This material undergoes a ferroelectric phase (FE-I phase) transition of displacive-type at 253 K followed by successive phase transitions to the lattice modulated phases with incommensurate periodicities and with commensurate 2-fold periodicity (FE-II phase) at lower temperature [2]. To elucidate the origin of the ferroelectricity in the FE-I phase, it is crucial to study the crystal structure using single crystals. The synchrotron x-ray diffraction experiment was carried out on the imaging-plate diffractometer at BL-8A of Photon Factory in KEK. Superstructure reflections with the modulation wave vector q=(1/2 1/2 1/2) were clearly observed below 103 K. Considering the preserved 2/m Laue symmetry, the lattice can be transformed to a C-centered monoclinic lattice, which is related by (-2a, -2b, a + c) or (2a, -2b, -a - c) with the FE-I structure. Although the lattice distortion and the intensities of the superlattice reflections are consistent with the 2/m Laue symmetry, the space group C1 is deduced from the polar nature and a subgroup symmetry of the FE-I structure. Moreover, we performed single-crystal neutron diffraction experiments at SENJU of MLF/J-PARC in order to determine the displacement of the hydrogen atom. The crystal structure analysis at 10 K was carried out using the reflections measured in a half-sphere of reciprocal space at d > 0.4. The structure analysis was performed on the basis of the space group C1, where four Phz and four H2ca become crystallographically inequivalent. Finally, all the structural parameters including all hydrogen atoms were successfully refined. In the FE-II phase, the neutral and ionic molecules alternately align along the π-molecular stack.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Acta Crystallographica Section A Foundations and Advances
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.