Structural study of electrodeposited aluminum-manganese alloys

Abstract

Aluminum-manganese alloys with compositions ranging between 0 and 27 wt pct Mn were electrodeposited at 150°C onto copper substrates from a chloroaluminate molten salt electrolyte with a controlled addition of MnCl2. The specimens were studied by scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), and X-ray diffraction. The addition of small amounts of Mn results in the formation of a supersaturated fcc solid solution of Mn in Al. At the higher Mn content, an amorphous phase is established. The highly faceted crystalline surface of pure Al and Al−Mn solid solution becomes smooth and nearly specular when the amorphous phase is present. The amorphous phase appears in the form of rounded grains and has a lower limit of Mn concentration close to the Al6Mn composition. There is a concentration discontinuity between the above limit and the higher Mn concentration limit of the fcc phase (about 9 wt pct). Appearance of the amorphous phase in the alloy results in a decrease in the Mn concentration in solid solution to about 2 wt pct. Crystallization of the amorphous phase starts at the fcc-amorphous phase interface at 230°C. As a result of treatment at 230 °C to 340 °C, the amorphous phase completely transforms into Al6Mn, while the fcc phase is unaffected. Prior to crystallization, the amorphous phase shows a modification that could be interpreted as the formation of a fine-grained icosahedral phase. The formation and distribution of phases by electrodeposition and rapid solidification are discussed.