Abstract
A significant cationic disorder is evidenced on Li3FeN2 prepared through solid-state reaction under controlled atmosphere. This derivative anti fluorite type structure (orthorhombic, space group Ibam, a=4.870(1)Å, b=9.652(1)Å and c=4.789(1)Å), solved first through single crystal X-ray diffraction [7], is usually described by Li+ and Fe+3 ordered distribution in tetrahedral sites formed by the nitrogen network, leading to [FeN4/2]3− edge-sharing tetrahedral chains. From 7Li/6Li Nuclear Magnetic Resonance spectroscopy, 57Fe Mössbauer spectroscopy and powder X-ray and neutron diffraction, we demonstrate that about 4% of lithium sites are filled by iron and about 11% of iron sites are occupied by Li, which can explain the discrepancy within the Gudat's model observed on larger scale solid-state synthesis samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.