Abstract
A study of the relationship between structure and growth parameters for existing and candidate carbon-based protective coatings has been carried out. In particular, diamond-like carbon (DLC) and carbon nitride thin films were deposited on silicon wafers by pulsed Nd:YAG laser (wavelength 532nm) ablation of graphite in high vacuum (p=1.5×10−7Pa) and in a nitrogen atmosphere (p=13Pa). The composition (N/C ratio), the structural and electronic properties and the surface morphology of the deposited films were investigated as a function of laser fluence (1–12J/cm2). The highest N/C ratio 0.40 was obtained with a laser fluence of 12J/cm2; for this nitrogen concentration X-ray photoelectron spectroscopy (XPS) reveals an increase of CN bonds instead of CN bonds with respect to lower concentrations.Electron energy loss spectroscopy (EELS) and XPS show an increase of sp2 carbon bonded sites in the DLC films deposited with lower laser fluences in agreement with the theory of the so-called sub-implantation model. EELS also reveals a gradient in the chemical nature of the films through the thickness. Atomic force microscopy analysis shows that the root-mean-squared roughness of the DLC samples is about 3Å over the laser fluence range investigated.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.