Abstract
The nanoStructured ZnO thin films were prepared by Spin coating technique on glass substrates at various layers. The structural and optical properties were characterized by field emission scanning electron microscopy (FESEM) and UV-Vis-NIR respectively. The surface morphology reveals that the nanostructured ZnO thin films become densely packed as the thickness increased. The average particles size of ZnO thin film estimated from FESEM images at different layers of 1, 3, 5, 7, 9 were 20nm, 28nm, 36nm, 39nm and 56nm, respectively. The surface roughness of thin films was increase as the thin film thickness increases. The results show all films are transparent in the visible region (400-800 nm) with average transmittance above 85 %. Meanwhile, the optical band gap was decrease as the film thickness increases. The conductivity of ZnO thin film slightly improved as the thickness increased as measured through two probes 1-V measurement system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.