Abstract
Modification in structural, optical and electrical properties of titanium nitride (TiN) thin films induced by argon ion irradiation and thermal annealings was studied using various experimental techniques. TiN thin films deposited by dc reactive sputtering on Si substrate were implanted with argon ions at 200keV. As-implanted samples were annealed before or after ion irradiation at 600°C and 700°C, respectively. Rutherford backscattering spectrometry, X-ray diffraction, cross-sectional (high-resolution) transmission electron microscopy, spectroscopic ellipsometry and electrical measurements were carried out in order to study structural, optical and electrical properties of TiN/Si samples. After irradiation with 200keV Ar ions the columnar microstructure of TiN was changed and the presence of smaller crystalline grains was observed. Partial loss of columnar structure observed in implanted samples was completely recovered after annealing at 700°C. Observed changes in microstructure induced by ion irradiation and annealings were correlated with the variation in optical parameters obtained by spectroscopic ellipsometry. It was found that both refractive index and extinction coefficient are strongly dependent on the defects' concentration and size of the crystalline grains in TiN layers.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Refractory Metals and Hard Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.