Abstract
This paper reports the effect of substrate bias on the structural, nanomechanical, and field emission properties of amorphous carbon films having embedded nanocrystallites (a-C:nc films) deposited by filtered anodic jet carbon arc technique. X-ray diffraction results exhibit predominantly an amorphous nature of the films. High-resolution transmission electron microscope images showed the amorphous nature of the films with nanocrystallites embedded in the amorphous matrix. Ultrafine nanograined microstructures with average grain size between 20 and 30 nm are observed throughout the film with a majority of the grains of single crystallites. A strong influence of substrate bias has been observed on the structural, nanomechanical, and field emission properties. Maximum nanohardness (H) of 58.3 GPa, elastic modulus (E) of 426.2 GPa, and H/E of 0.136 have been observed in a-C:nc films deposited at −60 V substrate bias which showed 82.6% sp3 content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.