Abstract
Niobium-carbide nanocomposite coatings with a carbon content varying from 43 to 64at.% were deposited by dual DC magnetron sputtering. X-ray diffraction, x-ray photoelectron spectroscopy and electron microscopy showed that all coatings consisted of nanometer sized NbC grains embedded in a matrix of amorphous carbon. Mechanical properties and electrical resistivity showed a strong dependency on the amount of amorphous carbon (a-C) and NbC grain size in the coating. The highest hardness (23GPa), elastic modulus (295GPa) and the lowest resistivity (260μΩcm) were measured for the coating with about 15% of a-C phase. Contact resistance measurements using a crossed cylinder set-up showed lowest contact resistance for the coating containing 33% a-C (140μΩ at a contact force of 100N), which is comparable to a Ag reference (45μΩ at a contact force of 100N). Comparison with TiC-based nanocomposites studied under similar conditions showed that the NbC system has less tendency to form a-C and that lowest contact resistance is obtained at comparable amounts of a-C phase in both material systems (33% for NbC compared to 35% for TiC). With these good electrical contact properties, the NbC nanocomposites can be considered as a potential material for electrical contact applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.