Abstract
The spinel Nano-ferrite system NiCrxFe2-xO4 (where x=0.0, 0.2, 0.4, 0.6, 0.8 and 1.0) have been prepared using flash auto combustion method. The XRD pattern confirms the formation of spinel Ni-Cr ferrite for the as-prepared samples. Electrical properties of as- prepared samples such dielectric constant and AC resistivity were studied in the temperature range (288- 773 K). It was observed that the AC resistivity increases by increasing Cr content and decreases by increasing frequency. The DC electrical resistivity was found to increase by increasing Cr content from 25*106 to 136*106 Ω.cm, whereas it was found to decrease with increasing temperature. VSM was used to study the magnetic properties of Ni-Cr ferrite at room temperature. It was found that, with increasing Cr content the (Ms) saturation magnetization decreased from 28 to 3 emu/g whereas coercivity increased from 188 to 666 (G).The magnetic moment of the system and Curie temperature decreased by increasing Cr substitution.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.