Abstract
In present work, we investigated the structural, magnetic, and electrical properties of Bi1.6Pb0.4Sr2Ca2Cu3O10+x superconductor prepared by using four different techniques: (i) solid-state (A), (ii) sol-gel (B), (iii) chemical wet (C), and (iv) melt-quench (D). From x-ray diffraction (XRD) and transmission electron microscopy (TEM) results, it is observed that the sintering process does not influence final crystallite size of compounds, but final crystallite sizes of the compounds were nearly the same after sintering process, while initial crystallite sizes were found to be different after the preparation process. From the XRD results, it is seen that the main phase in the compound is low-Tc Bi-(2212) phase and all samples contain a small amount of high-Tc Bi-(2223) phase. From scanning electron microscopy (SEM), two different types of surface crystallization of the compounds have been observed. The low-temperature resistivity, R(T), measurements show that all compounds have low zero resistivity, Tc,offset, value. Samples A, B, and C show the high-Tc and low-Tc transition at 110 and 75 K, respectively, while sample D displays only low-Tc transition at 75 K. These results have been supported by magnetization versus temperature measurement, M(T). In order to calculate critical current, Jc, values for the samples, magnetic hysteresis curves were taken at temperatures 10, 20, 30, 40, 50, and 60 K between the fields of ± 9 T. The hysteresis and the Jc calculation results show that sample D, when compared with other samples, has the best superconducting properties and has the highest Jc value. The best superconductivity properties between the studied samples have been obtained for sample A, while the best magnetic properties and the highest Jc value have been observed for sample D. According to the results obtained in this study, the structural and superconducting properties change with sample preparation method.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.