Structural investigation of xAg2O·(100−x)·[2B2O3·As2O3] glasses doped with manganese ions

Abstract

Structural analysis of x[(100−y)Ag2O·yMnO]·(100−x)[2B2O3·As2O3] glasses, with x=10mol% and 0≤y≤10mol%, was performed by means of FT-IR and FT-Raman spectroscopies. The purpose of this work is to investigate the structural changes that appear in the xAg2O·(100−x)·[2B2O3·As2O3] glasses with the addition and increase in manganese ions content. FT-IR measurements revealed the presence of pyro-, ortho-, di-, tri-, tetra- and penta-borate groups and structural units characteristic to As2O3 in the structure of the studied glasses. FT-IR spectroscopy measurements also show that BO3 units are the main structural units of the glass system. The presence of structural units characteristic to Ag2O were not directly evidenced by FT-IR spectroscopy. In addtition, the FT-Raman analysis evidenced the presence of boroxol rings in the structure of the studied glasses.