Abstract
The development of the structure of silica/alumina gels was investigated by small angle X-ray scattering (SAXS) through all stages of the preparation process, that is gelation, aging, drying and calcination. Two series of gels were compared; the first was prepared from a single-source precursor, obtained by reaction of 3-oxoethyl-6-trimethoxysilyl-hexan-2-one (OTH-H) with Al(O s Bu) 3. The gels of the second series were prepared from the same precursors, but under conditions where hydrodeacylation of OTH-H occurs. It turned out that both series showed a similar structural development of the gels. Immediately after the start of the reaction small primary particles are formed, the size of which ( r = 0.7 ± 0.1 nm) remains constant through the gelation and aging process. In some samples, Si(OEt) 4 was added as an additional source for Si/O which was incorporated between the primary particles. Condensation proceeds by a slower aggregation of the primary particles, which initially form a rather open network. This network densifies during aging and drying.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.