Structural influence of mixed transition metal ions on lithium bismuth borate glasses

Abstract

Lithium bismuth borate glasses containing mixed transition metals having composition 7CoO·23Li2O·20Bi2O3·50B2O3 (CLBB), 7V2O5·23Li2O·20Bi2O3·50B2O3 (VLBB) and x(2CoO·V2O5)·(30 - x)Li2O·20Bi2O3·50B2O3 (x = 0.0 (LBB) and x = 2.0, 5.0, 7.0, 10.0 mol% (CVLBB1-4)) are synthesized via melt quench route. The synthesized compositions are investigated for their physical properties using density (D) and molar volume (Vm), thermal properties by analyzing DSC/TG thermo-graphs, structural properties using IR absorption spectra in the mid-IR range and optical properties using UV–Vis–NIR spectroscopy. The Electron Paramagnetic Resonance (EPR) spectra of vanadyl and cobalt ion have been analyzed to study compositional effects on spin-Hamiltonian parameters. The non linear variations in physical properties depict a strong structural influence of Co/V- oxides on the glassy matrix. The compositional variations in characteristic temperatures (glass transition temperature Tg, glass crystallization temperature Tp and glass melting temperature Tm) reveals that Tg for glass samples CLBB is relatively less than that of pure lithium bismuth borate (LBB) glass sample wherein Tg for sample VLBB is higher than that of LBB. The increase in Tg (as compared with LBB) with an enhanced substitution of mixed transition metal oxides (2CoO·V2O5) shows a progressive structure modification of bismuth borate matrix. These predictions are very well corroborated by corresponding compositional trends of Tp and Tm. FTIR studies reveal that Co2+& VO2+ ions lead to structural rearrangements through the conversion of three-coordinated boron into four coordinated boron and thereby reducing number of non-bridging oxygen atoms. Bismuth is found to exist in [BiO6] octahedral units only, whereas boroxol rings are not present in the glass network. The theoretical values of optical basicity (Λth) and corresponding oxide ion polarizability (αo2−) have also been calculated to investigate oxygen covalency of glass matrix. Trends in both these parameters suggested an increase in ionic bonding on substitution of divalent transition metal cations causing a more bonding compaction in glass structure. The UV–Vis–NIR spectra suggest that cobalt ions exist as Co2+ states in octahedral coordination in glass network. Inter-electronic repulsion parameter and crystal field splitting energy were evaluated to understand the site symmetry around Co2+-ion in glass. X-band EPR spectra suggest that vanadium ions (V4+) exists as VO2+-ions in octahedral coordination with tetragonal compression. Spin Hamiltonian parameters g-values and A-values of VO2+ ions in glass were calculated. For sample CLBB two resonance lines in EPR spectrum attribute to octahedral symmetry around Co2+-ions were observed.