Abstract
Lithium fluoro zinc borate (LBZ) glasses doped with Nd3+ ions at distinct concentrations (0.3, 0.5, 1 & 1.5mol%) were prepared using melt quenching technique. Structural, thermal and compositional studies of these glasses were carried out by XRD, TG-DTA and FTIR analysis respectively. The properties of dielectric studies such as dielectric constant and dielectric loss have been studied systematically as a function of frequency. The ionic conductivity of Nd3+: LBZ doped glasses have been found to be more than the conductivity of the host LBZ glass and the optimized concentration of 0.5mol% Nd3+: LBZ glass exhibits high ionic conductivity. Photoluminescence proerties of obtained glasses were systematically analyzed. J-O intensity Ωλ (λ=2, 4, 6) parameters have been evaluated from the absorption spectrum of 0.5mol% Nd3+: LBZ glass and they were used to estimate the parameters such as radiative lifetime (τR), transition probability (A), branching ratios (βR) and spectroscopic quality factor (χ) for the major emission transitions. Predominant NIR emission at 1062nm (4F3/2→4I11/2) is observed under the excitation of 741nm (4I9/2→4F7/2) along with other two moderately less intense emission peaks at 897nm (4F3/2→4I9/2) and 1332nm (4F3/2→4I13/2). Experimental lifetime for the level 4F3/2 has been compared with radiative lifetime obtained through J-O parameters. The decay lifetimes dynamics and non-radiative transition rate have been systematically evaluated. These Nd3+ doped glasses could be suggested as promising candidates for 1.06μm laser applications and solid state battery applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.