Abstract
The optical and structural characteristics of GaN films implanted with Mg and Be ions, grown by low-pressure metalorganic chemical vapor deposition were studied. The low temperature (20 K) photoluminescence (PL) spectra of annealed Mg implanted GaN show a 356 nm near band edge emission, a 378 nm donor-acceptor (D-A) transition with phonon replicas, and a 528 nm green band deep level emission. The origin of the 528 nm green band emission and the 378 nm D-A emission might be attributed, respectively, to the Mg implantation induced clustering defect and the vacancy defect in GaN film. Observations of in-plane and out-of-plane x-ray diffraction spectra for as-grown undoped, Mg implanted and rapid thermal annealed GaN suggest that ion implantation induced anisotropic strain may be responsible for the observed PL emission characteristics.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.