Abstract
In this work, some surface properties of AISI M2 steel were improved by a thermoreactive deposition process. Gas nitriding was realized on AISI M2 steel at 550°C for 2 h in an ammoniac atmosphere and then, titanizing treatment performed on pre-nitrided steel in the powder mixture consisting of ferro-titanium, ammonium chloride and alumina at 1000°C for 1-4 h. Structural characterization of titanium nitride layer formed on the surface of AISI M2 steel was carried out by using optical microscopy, scanning electron microscopy, electron microprobe and Xray diffraction (XRD) analysis. The hardness measurements of titanium nitride layer were conducted under 10 g loads by using Vickers microhardness indenter. Structural analysis studies showed that titanium nitride layers formed on the AISI M2 steel samples were smooth, compact and homogeneous. XRD analysis show that the coating layer formed on the steel samples includes TiN, Fe6Mo7N2, C0.7N0.3Ti, C0.3N0.7Ti and V2N phases. The hardness of titanium nitride layers formed on the steel samples is between 2040±186 and 2418±291 HV0.01. The thickness of titanium nitride layer formed on the steel samples ranged from 3.86±0.43 9m to 6.13±0.47 9m, depending on treatment time.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.