Abstract
Optically active 2mol% dysprosium doped zirconia, Zr0.98Dy0.02O2, was synthesised by conventional solid state route. Rietveld analysis of XRD data of this composition revealed that monoclinic phase dominates at room temperature. SEM micrograph depicted the presence of spherical grains with average grain size of 200nm. The FTIR spectrum of this system indicated a homogeneous distribution of Dy particles among the zirconia structure. The Raman and UV spectra of the system showed various peaks corresponding to different phases present in the system. The electrical conductivity and dielectric properties of this system were measured in temperature range 573–1073K and in the frequency range 20Hz–1MHz. The real part of conductivity spectra was found to follow Jonscher power law. The temperature dependent total conductivity was found to show three different regions, with different activation energy in the entire temperature range. The scaling behaviour of the conductivity spectra also confirms the observed temperature dependence. The temperature and frequency dependence of real part of permittivity and tangent loss indicated the presence of orientational and space charge polarization processes in the system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.