Abstract
The structure, IR absorption, luminescence, and luminescence excitation spectra of La0.99-xYxEu0.01BO3 orthoborates synthesized at 970oC were studied at 0≤ x≤0.99. An increase in x leads to a sequential change of the structural state of these compounds. At 0≤ x≤0.1, the samples are single-phase and have the aragonite structure. Within the range of 0.1<x≤0.8, the samples are two-phase: the vaterite phase is observed along with the aragonite structure. At 0.8<x≤0.99, the samples are single-phase and have the vaterite structure. Correspondence between the structure and spectral characteristics of these compounds was established. It is demonstrated that with an increase in the Y3+ concentration, the vaterite phase is formed first in the bulk of microcrystals having the aragonite structure and then in the entire sample. It is shown for the first time that a band with the maximum of 469 nm is observed in the luminescence excitation spectrum (LES) of samples having the vaterite structure and is absent in samples having the aragonite structure. It is revealed that a band in the luminescence spectrum, corresponding to the ^5D_0->^7F0 electron transition, as well as 469 nm-band in the LES, can be an indicator of the structural state of the sample. Keywords: rare earth orthoborates, X-ray diffraction analysis, crystal structure, IR spectroscopy, luminescence spectra.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.