Abstract
We report a modification of nanostructured WO3 films by doping with boron. The films were obtained by a direct one-step sol–gel route involving tungstic acid/polyethelene glycol precursor. Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) showed that the incorporation of boron results in the retention of a substantial amount of water and/or hydroxyl groups in the WO3 lattice and at the surface of nanoparticles occurring despite high temperature (550°C) annealing of the films. Another consequence of boron doping is the largely increased roughness factor revealed by atomic force microscopy (AFM) imaging. Both kinds of films are highly porous and consist of partly sintered particles with sizes in the range of tens of nanometers. The photoelectrochemical (PEC) studies performed under simulated solar AM 1.5 illumination showed significantly enhanced water oxidation photocurrents for B-WO3 photoanodes, by about 25% higher than those for the undoped WO3 films of similar thickness. The low extent of recombination of photogenerated charges was confirmed by incident photon-to-current conversion efficiencies (IPCEs) reaching 70% in the region of visible wavelengths at 420nm. The improved PEC properties were attributed to the increased surface hydroxylation of B-WO3 nanoparticles favoring water photo-oxidation reaction and to the larger surface area of the film exposed to the electrolyte.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.