Abstract
Using transmission electron microscopy, X-ray diffraction analysis, Mossbauer spectroscopy, microdurometry, and microindentation, the effect of large plastic deformations (through shear under pressure in Bridgman anvils) on the structure, phase composition, and micromechanical properties of high-nitrogen (1.24 wt % N) 08Kh22GA1.24 steel has been investigated. The steel was obtained by the casting method with counterpressure of nitrogen and was subjected to different heat treatments (quenching from1180°С, aging at 450 and 550°С) that form an austenitic (FCC) structure of the metallic matrix with chromium nitrides. It has been established that deformation by shear under pressure at room temperature results in the dispersion and deformation-induced partial dissolution of primary nitrides Cr2N in quenched and aged steel and in the complete (after aging at 450°С) and partial (after aging at 550°С) dissolution of secondary nitrides CrN. It has been noted that, for aged steel that contains finely dispersed secondary chromium nitrides upon shear deformation, as compared to the quenched state, the dispersion of the austenitic structure (down to nano- and submicrocrystalline states) is more intense and the enhancement in the microhardness and resistance to elastic–plastic deformations upon contact loading is more effective.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.