Abstract
Tin-doped indium oxide (ITO) thin films were fabricated by the sol–gel spin-coating method with different indium precursor solutions synthesized from In(NO 3) 3 or InCl 3 (denoted as N-ITO and Cl-ITO, respectively). For both N-ITO and Cl-ITO thin films, the increase of mobility/conductivity and the reduction of carrier concentration with increasing annealing temperatures from 400 to 700 °C are related to the increase of crystallization/densification and the annihilation of oxygen vacancies. The refractive index (1.84 at λ = 550 nm), packing density (0.83), conductivity [(234 (Ω-cm) − 1 ], and optical band gap (3.95 eV) of N-ITO thin films are higher than that of Cl-ITO thin films, which can be attributed to the higher densification, lower crystallinity, and more free charge carriers of N-ITO thin films. These properties make the indium nitrate-derived ITO thin films have better potential applications for some commercial products.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.